Two sets of formulations based on three copolymer and three terpolymer systems involving tributyltin methacrylate(BTMA),methyl methacrylate(MMA) and acrylonitrile (AN) with variable tin contents of 7, 15 and 22% were prepared. There is only one varient in each formulation of the six prepared, that is the type of organotin polymer whether it is a copolymer or terpolymer of a definite tin content 7 or 15 or 22%. The binder mixture is a blend consisting of the organotin polymer, a vinyl copolymer and its external plasticizer and little amount of rosin. A moderate and fixed amount of cuprous oxide was introduced into all formulations as a supplementary toxin with organotin polymer. Leaching rates of micro amounts of copper and tin were determined. Panel exposure test in the sea was performed at Port Said. Best antifouling efficiency was obtained from formultions containing organotin copolymer or terpolymer of 22% tin content and that containing organotin copolymer of 15% tin.

The effect of pigment filler and extender on the antifouling efficiency of six compositions containing organotin polymer is studied. The binder mixture is a blend containing a copolymer of tri‐n‐butyltin methacrylate and methylmeth acrylate (OTP) with 22% tin content, a vinyl copolymer with its external plasticizer and little amount of rosin. Cuprous oxide was added as a supplementary toxin with the OTP. Leaching rates of microamounts of copper and tin were determined for a period of nearly one year applying standard techniques. Painted plates were immersed in Suez Canal waters at Port‐Said for more than 36 months. Comparison between different fillers and extenders on the antifouling behaviour of painted surfaces is shown. Compositions containing cellite and china clay exhibited the maximum antifouling performance.